DYNAFLOW |
 |
 BRAZING PROPERTIES:
Designed for copper or brass applications, Dynaflow is self
fluxing on copper but requires use of Stay-Silv® white or
black brazing flux when joining brass.
Dynaflow mirrors the brazing characteristics of
Stay-Silv® 15. The melting range is wide enough to allow
filling gaps, necessary to braze loose connections or “cap” a finished joint. When heated to its liquidus temperature
the filler metal flows quickly to fill tight gaps or standard connections. |
| |
CHEMICAL COMPOSITION |
Silver |
5.9-6.1% |
Copper |
Remainder |
Phosphorus |
6.08% |
Other Totals |
0.15% |
PHYSICAL PROPERTIES |
Solidus |
1190°F (643°C) |
Liquidus |
1459-1471°F (787-794°C) |
Tensile Strength-Brazed Copper |
35,000 psi nominal, based on (242 mm²-tube alloy C122 annealed.) |
Braze Color |
Gray |
Electrical Conductivity |
(%IACS) 8.80 |
Electrical Resistivity |
19.7 |
AVAILABLE FORMS:
Standard rod diameters in 20” or 36” lengths
Preformed rings
Layer wound spools
RECOMMENDED FLUX:
No flux required on copper
Stay-Silv® white or black brazing flux with brass
SPECIFICATION COMPLIANCE:
Harris Products Group proprietary specification. |
|
STATEMENT OF LIABILITY — DISCLAIMER |
| Any suggestion of product applications or results is given without representation or warranty, either expressed or implied. Without exception
or limitation, there are no warranties of merchantability or of fitness for particular purpose or application. The user must fully
evaluate every process and application in all aspects, including suitability, compliance with applicable law and non-infringement of the
rights of others. The Harris Products Group and its affiliates shall have no liability in respect thereof. |
|
|
 |
|
4501 Quality Place