SS6HP 3/32 Dia x 36 x 25lbs PKG

Diámetros / Embalaje

Diámetros
mm
25 lb Box
1/8 in (3.2 mm) 6H636R
3/32 in (2.4 mm) 6H536R
3/32 x 3/32 in (2.4 x 2.4 mm) 6H536S

Stay-Silv® 6HP

Phos-copper-silver filler metal with a medium temperature range for brazing copper-to-copper and copper-to-brass with the use of flux for assemblies with wider clearances.

Detalles

Stay-Silv® 6HP is slightly more fluid and can be used where closer tolerances are available. It is somewhat more ductile than Harris® 0.

Características

  • Medium range silver brazing filler metal designed for copper-to-copper applications
  • Can also be used on copper-to- brass with appropriate brazing flux
  • Has lower phosphorus content creating an alloy well suited for many brazing applications. The melting range makes it useful for assemblies with wider clearances.
  • Often used in rod form for manual braze applications, but is a good choice to be formed as brazing rings or on spools for semi-automated applications.
  • Corrosion resistance is generally similar to copper base metal, but phosphorus containing alloys, including Stay-Silv® 6HP, should not be used if the braze is exposed to sulfur or sulfur compounds in service
  • Medium range alloy is well suited where close fit-up cannot be maintained. Filler metal is somewhat more ductile than Stay-Silv® 2.
  • Not recommended for brazing steel or other ferrous base metals, as the phosphorus content promotes formation of low ductility intermetallic with the base metal.
  • For copper-to-copper and copper-to-brass applications using Stay-Silv® white brazing flux.
  • Complies with the EU Reach & RoHS directive

Aplicaciones Típicas

  • Brass brazing