STAY-SILV 15 Pho Copper Alloy
SS15-.050X1/8X20X28 STICK TUBE X 5 PACK

Diameters / Packaging

Diameters
 1 ea Tube
 1 lb Box
 5 lb Tube
 5 pk Tube
 10 lb Tube
 25 lb Box
15S0051
0.050 x 1/8 in (1.3 x 3.2 mm) 15620F1,1520FMPOP 15620F5 15620F15P 15620F,15636F
0.050 x 1/16 in (1.3 x 1.6 mm) 15320F1 15320F
1/8 in (3.2 mm) 15620R1 15636R
1/8 x 1/8 in (3.2 x 3.2 mm) 15620S1 15636S10 15620S,15636S
1/16 in (1.6 mm) 15320R1 15320R,15336R
3/32 in (2.4 mm) 15520R1 15520R,15536R
3/32 x 3/32 in (2.4 x 2.4 mm) 15520S,15536S

Stay-Silv® 15 Phos-Copper Brazing Alloy

15620F15P

Stay-Silv® 15 phos-copper brazing alloy 0.050 x 1/8 x 20 in. x 5 ea. 28-stick tubes

Diameter

Select Diameter

  • 0.050 x 1/8 in (1.3 x 3.2 mm)
  • 0.050 x 1/16 in (1.3 x 1.6 mm)
  • 1/8 in (3.2 mm)
  • 1/8 x 1/8 in (3.2 x 3.2 mm)
  • 1/16 in (1.6 mm)
  • 3/32 in (2.4 mm)
  • 3/32 x 3/32 in (2.4 x 2.4 mm)

Package

Select Package

  • 1 ea Tube
  • 5 lb Tube
  • 5 pk Tube
  • 25 lb Box

DETAILS

Stay-Silv® 15 phos-copper filler metal is the industry standard for air conditioning/refrigeration applications. Its melting range is useful in filling wider clearances while providing good service ductility. Complies with the EU Reach & RoHS directive.

Features

  • Popular choice for copper brazing air conditioning and refrigeration connections
  • Flows into tight connections when heated above its liquidus temperature
  • Wide melting range allows operators to fill loose connections and "cap" or "build-up" around the finished joint. When heated above its liquidus it will penetrate tight connections.
  • Popular brazing filler metal for HVAC and refrigeration connections
  • Recommended joint clearance of 0.003 in. - 0.006 in. (0.08 mm - 0.15 mm)
  • Flux not required for copper brazing as it is self-fluxing. For brazing brass or copper-to-brass Stay-Silv® white flux is suitable for most applications. Harris Eco Smart® boric acid free flux, powder or paste, is an excellent choice to promote sound brazed assemblies
  • Corrosion resistance is generally similar to the copper base metal, but phosphorus containing alloys, including Stay-Silv® 15, should not be used if the braze is exposed to sulfur or sulfur compounds in service
  • Not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility
  • Suitable for brazing low nickel (10% maximum) copper/nickel base metals
  • Complies with the EU Reach & RoHS directive